2013/09/29

1.1181

                                                                               1.1181
Data Table for Steel Grades:1.1181
Mechanical Properties of Materials of grade steel:1.1181
Tensile strength, Flexural strength, Compressive strength, Shear Strength, Tensional strength, Reduction area, Yield Strength, Elongation. 
Chemical composition % of the ladle analysis of steel grade:1.1181

Chemical composition %   of grade   C35E (1.1181)
Cr + Mo + Ni = 0.63
CSiMnNiPSCrMo
0.32 - 0.39max   0.40.5 - 0.8max   0.4max   0.03max   0.035max   0.4max   0.1


Mechanical properties of grade   C35E (1.1181)

Nominal thickness (mm):  to 1616 - 100100 - 250250 - 500500 - 1000
Rm - Tensile strength (MPa) (+N)550520500480470
Nominal thickness (mm):  0.3 - 3
Rm - Tensile strength (MPa) (+A)540
Nominal thickness (mm):  0.3 - 3
Rm - Tensile strength (MPa) (+CR)930
Nominal thickness (mm):  5 - 1010 - 1616 - 4040 - 6363 - 100
Rm - Tensile strength (MPa) (+C)650-1000600-950580-880550-840520-800
Nominal thickness (mm):  to 88 - 2020 - 5050 - 80
Rm - Tensile strength (MPa) (+QT)630600550500


Nominal thickness (mm):  to 88 - 2020 - 5050 - 80
ReH - Minimum yield strength (MPa) (+QT)430380320290


Nominal thickness(mm):  to 1616 - 100100 - 250
Re - Upper yield strength or
Rp0.2 - 0.2% proof strength (MPa) (+N)
300270245
Nominal thickness(mm):  0.3 - 3
Rp0.2 0.2% proof strength (MPa) (+A)430
Nominal thickness(mm):  to 100100 - 250250 - 500500 - 1000
Re - Upper yield strength (MPa) (+N)270245220210
Nominal thickness(mm):  5 - 1010 - 1616 - 4040 - 6363 - 100
Rp0.2 0.2% proof strength (MPa) (+C)510420320300270


KV - Impact energy (J) (+QT)+20°
35
KV - Impact energy (J) (+N)+20°
27
KV - Impact energy (J) transverse, (+QT)+20°
22


A - Min. elongation at fracture (%) transverse, (+N)15
Nominal thickness (mm):    5 - 1010 - 1616 - 4040 - 6363 - 100
A - Min. elongation at fracture (%) (+C)67899
Nominal thickness (mm):    to 88 - 2020 - 5050 - 80
A - Min. elongation at fracture (%) longitud., (+QT)17192020
A - Min. elongation at fracture (%) longitud., (+N)21
A - Min. elongation at fracture (%) longitud., (+A)22


Nominal thickness (mm):    to 1616 - 100100 - 250
A - Min. elongation Lo = 5,65 √ So (%) (+N)181919


  Brinell hardness   (HBW):   (+SH)154 - 207
  Brinell hardness   (HBW):   (+A)183
  Vickers hardness  ( HV):   (+CR)275
  Vickers hardness  ( HV):   (+A)170


Properties of grade   C35E (1.1181)
Weldability: It can be welded quite well without any precautions.
Hardenability: Low hardenability; core quenching in water till a diameter of 12-15 mm; as far as bigger diameters are concerned, it hardens only till a certain depth, inversely proportional to diameter, like all nonalloy steels with medium-high carbon content.
Technological properties of grade steel:1.1181
Hardness and heat treatment specification of steel grade:1.1181

Mechanical Properties,Hardness and heat treatment specification.Machinability,Welding,Hot Working,Cold Working, Annealing,Tempering,Hardening,Heat treatment,etc.
salt-bath furnacecontrolled atmosphere furnace
235262788119112045~15air cooling52260
longitudinalhorizontal
Hot-rolled/Cold rolling:5 - 15052041516~182a3.5a
Note:
(1) listed in the table apex diameter (d), to steel thickness (a) multiples said.
(2) in the ASTM A6 standard specified scope can meet any additional conditions.
(3) from the standard for 50 mm (2 in).
Mechanical properties of Manusteelcn.
Mechanische Eigenschaften of Manusteelcn.
Caracteristiques mecaniques of Manusteelcn.
ReH Minimum yield strength / Mindestwert der oberen Streckgrenze / Limite d’elasticite minimale
Rm Tensile strength / Zugfestigkeit / Resistance a la traction
A Minimum elongation / Mindestwert der Bruchdehnung / Allongement minimal
J Notch impact test / Kerbschlagbiegeversuch / Essai de flexion par choc
Manusteelcn——China steel suppliers - Superior technology, Advanced equipment, Perfect procedure!

Steel description: Manusteelcn.
Step Shaft: steel plate/sheet,coil,round bar,flat bar,tube/pipe,Profiled forgings
Manusteelcn steel Specifications or Size:
Diameter : 1mm-2000mm
Size: 50mm * 50mm-600mm *600mm
Size: Thickness: 0.1mm-800mm Width: 10mm to 1500mm
Size: OD: 6-219mm WT: 1-35 mm.
Cold-rolled sheet: Thickness: 2-5mm Width:1000mm Length: 2000mm
Hot-rolled sheet: Thickness:6-80mm Width: 210-610mm
Length: We can supply any length based on the customer's requirement.
Forging/hot rolling/ extrusion of steel.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processingelectrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any in-perfections or based on the customer's requirement.
UTS according to SEP 1921 C/c,D/d,E/e;A388 or GB/T 6402
Excellent service for all kinds of industries, with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and Professionality.

Hot keywords of steel grade:
1.1181


Contact:Daniel Zhao,
Skype:manusteelcn
Tel:+86-15390275258
Fax:+86-816-3639422



        Further reading


The United States standard grade of steel representation methodAISIACIASTM, SAE,UNS,ANSI,
ASME,SWS.
The German standard grade of steel representation method:DIN.
The Japan standard grade of steel representation method:JIS.
The Britain standard grade of steel representation method:BS.
The France standard grade of steel representation method:NF.
The Russia standard grade of steel representation method:ΓOCT.
The China standard grade of steel representation method:GB/T 221—2000/GB/T 17616—1998.
The Korea standard grade of steel representation method:KS.
The Taiwan(China) standard grade of steel representation method:CNS.
The Sweden standard grade of steel representation method:SS(SIS).
The international organization for standard grade of steel representation method:ISO.
If you need more information for standard grade of steel representation method,pls click here.


Use of steel
Iron and steel are used widely in the construction of roads, railways, other infrastructure, appliances, and buildings. Most large modern structures, such as stadiums and skyscrapers, bridges, and airports, are supported by a steel skeleton. Even those with a concrete structure employ steel for reinforcing. In addition, it sees widespread use in major appliances and cars. Despite growth in usage of aluminium, it is still the main material for car bodies. Steel is used in a variety of other construction materials, such as bolts, nails, and screws.
Other common applications include shipbuilding, pipeline transport, mining, offshore construction, aerospace, white goods (e.g. washing machines), heavy equipment such as bulldozersoffice furniture, steel wool, tools, and armour in the form of personal vests or vehicle armour (better known as rolled homogeneous armour in this role). Steel was the metal of choice for sculptor Jim Gary and a frequent choice for sculpture by many other modern sculptors.
Typical Mechanical Properties
Related Terms of steels
Usage of Steel.
Firstly, The structuralsteel,
1>The construction and engineering with the  structural steel is called  construction steel, it is used in building, bridges, ships, boilers or other engineering, it is the production of the metal structure of the steel. Such as carbon steellow alloy steelreinforced steel.
2>     Machinery manufacturing structural steel- steel structural parts for manufacturing machinery and equipment. For his style of steel, it  is basically a high-quality steel or high-quality steel, mainly has quality carbon structural steel, alloy structural steel, easy to cut structural steel, spring steel, bearing steel, etc.  
Generally used in the manufacture of a variety of tools, such as carbon tool steel, alloy tool steel, high speed tool steel, etc. According to the usage, it can be divided into cutting tool steel, die steel, gauge steel.
Steel with special properties, such as acid-resistant stainless steel, heat cannot afford leather steel, high resistance alloy  steel, wear-resistant steel, magnet steel, etc.
This means the steel professional use of the various industrial sectors, such as automotive steel, farm machinery steel, aviation and steel, chemical machinery steel, boiler steel, electrical steel, welding rod steel.
(1)Ordinary steel, more elements containing impurities in the steel, P O.05%,S 0.045%,such as carbon steel, low-alloy structural steel, etc.
(2)Quality steel, less elements containing impurities in the steel 0.04%,S 0.04%, such as high-quality carbon structural steel, alloy structural steel, carbon tool steel and alloy tool steel, spring steel , bearing steel ,etc.
(3) High quality steel, fewer elements containing impurities in the steel ,S O.03%,P  0.035%, such as alloy structural steel and tool steel. High quality steel behind the steel grade, it is usually added the symbol "A" or the Chinese character "high" in order to be recognized.

Delivery Status of steel,
   Reliability,Trustworthiness.Hand in hand!We work together and build a long mutual business relationship with you for the steel grade!Warmly welcome!


For more information of steel,pls click here.

No comments:

Post a Comment